This monograph is written based on the author's research on the assessment, control, and repair of cracking of early-age concrete in the recent decade. The technique of internal curing for increasing cracking resistance of early-age concrete is further developed through experimental and theoretical research. It establishes models for predicting the internal relative humidity and autogenous shrinkage of internally cured concrete at early age; reveals the variation law and mechanism of early-age tensile creep of internally cured concrete; and explores the variation law and mechanism of early-age cracking resistance of internally cured concrete under continuous restrained condition or uniaxial restrained condition. It is designed as a reference work for professionals or practitioners and a textbook for undergraduates or postgraduates. As such, this book provides valuable knowledge, useful methods, and practical experience that can be considered in the field of concrete cracking control.
CREEP, SHRINKAGE AND DURABILITY MECHANICS OF CONCRETE AND CONCRETE STRUCTURES contains the keynote lectures, technical reports and contributed papers presented at the Eighth International Conference on Creep, Shrinkage and Durability of Concrete and Concrete Structures (CONCREEP8, Ise-shima, Japan, 30 September - 2 October 2008). The topics covered
This is the state-of-the-art report prepared by the RILEM TC “Application of Super Absorbent Polymers (SAP) in concrete construction”. It gives a comprehensive overview of the properties of SAP, specific water absorption and desorption behaviour of SAP in fresh and hardening concrete, effects of the SAP addition on rheological properties of fresh concrete, changes of cement paste microstructure and mechanical properties of concrete. Furthermore, the key advantages of using SAP are described in detail: the ability of this material to act as an internal curing agent to mitigate autogenous shrinkage of high-performance concrete, the possibility to use SAP as an alternative to air-entrainment agents in order to increase the frost resistance of concrete, and finally, the benefit of steering the rheology of fresh cement-based materials. The final chapter describes the first existing and numerous prospective applications for this new concrete additive.
Curing is one of those activities that every civil engineer and construction worker has heard of, but in reality does not worry about much. In practice, curing is often low on the list of priorities on the construction site, particularly when budgets and timelines are under pressure. Yet the increasing demands being placed on concrete mixtures also
This is the state-of-the-art report prepared by the RILEM TC “Application of Super Absorbent Polymers (SAP) in concrete construction”. It gives a comprehensive overview of the properties of SAP, specific water absorption and desorption behaviour of SAP in fresh and hardening concrete, effects of the SAP addition on rheological properties of fresh concrete, changes of cement paste microstructure and mechanical properties of concrete. Furthermore, the key advantages of using SAP are described in detail: the ability of this material to act as an internal curing agent to mitigate autogenous shrinkage of high-performance concrete, the possibility to use SAP as an alternative to air-entrainment agents in order to increase the frost resistance of concrete, and finally, the benefit of steering the rheology of fresh cement-based materials. The final chapter describes the first existing and numerous prospective applications for this new concrete additive.
Early age cracking of bridge decks is a national problem, and may substantially reduce service lives and increase maintenance costs. Cracking occurs when the tensile stress exceeds the tensile strength of the concrete. This is a time-dependent phenomenon, since both the stress and strength change at early ages. Moisture loss increases stress (with increasing shrinkage) and impairs strength gain. Internal curing is one method that has been suggested to reduce early age bridge deck cracking, particularly of concretes with low water to cementitious materials (w/cm) ratios. Many state highway agencies have implemented high performance concrete (HPC) for bridge decks. The low permeability of HPC is used to protect reinforcing steel and prevent corrosion. However, if the concrete cracks, then the protection may be greatly diminished. Transverse cracks due to concrete shrinkage allow water and corrosive chemicals to quickly reach the reinforcing steel causing corrosion and shortening the lifespan of the bridge deck. Reducing shrinkage cracking has been the focus of recent research into mitigation strategies. One unintended consequence of the use of high performance concrete may be early-age cracking. Field studies have shown that, in some cases, high performance concrete bridge decks have cracked less than a year after placement. The use of internal curing to reduce autogenous shrinkage was investigated in this study. One method of internal curing was through the use of coarse aggregates with high absorption capacities. Another method discussed is the use of a partial replacement of the fine aggregate with a structural lightweight aggregate with a very high absorption capacity. Bridge deck cracking is also affected by the nominal maximum size coarse aggregate. The effect on shrinkage with increasing size is discussed. ODOT's District 12, located in Northeastern Ohio, found in an investigation of 116 HPC bridge decks placed between 1994 and 2001 that bridges with little or no cracking used coarse aggregate with an absorption> 1 %, while 75 % of bridges with unacceptable cracking used coarse aggregate with absorption 1 %. This report discusses the laboratory investigation of the field results to determine the better ways to prevent bridge deck cracking-- internal curing or paste reduction by using an aggregate blend. The laboratory investigation found that the strongest effect on cracking was due to the replacement of a small maximum size coarse aggregate with an optimized coarse aggregate gradation. Increasing the coarse aggregate absorption level from
This book presents the latest research advances and findings in the field of smart/multifunctional concretes, focusing on the principles, design and fabrication, test and characterization, performance and mechanism, and their applications in infrastructures. It also discusses future challenges in the development and application of smart/multifunctional concretes, providing useful theory, ideas and principles, as well as insights and practical guidance for developing sustainable infrastructures. It is a valuable resource for researchers, scientists and engineers in the field of civil-engineering materials and infrastructures.
The design of concrete mixes is becoming increasingly complex, with the addition of new materials in the compounds, such as organic admixtures, fibres and supplementary cementitious materials. Moreover, the list of properties which concretes are required to possess for certain applications has increased, and interest is developing in rheology, durability, deformability and whole-life behaviour. This book presents a number of simple models for the understanding of a concrete system, and provides the techniques for developing more sophisticated models for the practical design of concrete mixes.