This Standard specifies the requirements, test methods, inspection rules, marking, package, transportation, storage, quality certificate, ordering list (or contract) contents of the high titanium slag. This Standard is applicable to the high titanium slag used by titanium tetrachloride, artificial rutile and titanium pigment with titanic iron ore as raw materials, and producing by electric furnace smelting.
This Standard specifies the requirements, test methods, inspection rules, marks, package, transportation, storage, quality certificate and orders (or contracts) for the tungsten concentrate. This Standard applies to tungsten concentrate products selected in mine; it can be used for producing ammonium paratungstate, tungstic acid, ammonium metatungstate, tungsten oxide etc.
This standard specifies the requirements, test methods, inspection rules and marking, packaging, transportation, storage, quality certificate and order form (or contract) content of O-Isopropyl-N-ethyl thionocarbamate. This standard applies to O-Isopropyl-N-ethyl thionocarbamate flotation reagents, which are synthesized from isopropyl xanthate, monochloroacetic acid, sodium carbonate, monoethylamine as raw materials.
This standard specifies the method for the determination of silicon, manganese, phosphorus, iron, copper, cobalt, magnesium, aluminum, zinc and chromium content in refined nickel by using an inductively coupled plasma atomic emission spectrometric method. This method is applicable to the analysis of silicon, manganese, phosphorus, iron, copper, cobalt, magnesium, aluminum, zinc and chromium content in refined nickel. The measuring range of each element is shown in Table 1. Table 1 -- Measuring range of each element Element Measuring range (mass fraction)/% YS/T 1085-2015 www.ChineseStandard.net ? Buy True-PDF ? Auto-delivery Page 5 of 16 2 Method principle A certain amount of the sample is weighed and decomposed by the nitric acid; an inductively coupled plasma atomic emission spectrometer is used to measure the spectral intensity of the spectral line of the element to be measured in the solution; the spectral line is corrected by subtracting the background to eliminate the influence of the matrix nickel; the elemental content is obtained from the calibration curve drawn according to the standard solution. 3 Reagents Unless otherwise stated, the reagents used in this standard are all of analytical grade, and the water used is first-grade water. 3.1 Nitric acid (¦Ñ=1.42 g/mL). 3.2 Nitric acid (1+1). 3.3 Hydrofluoric acid (¦Ñ=1.15 g/mL). 3.4 Silicon standard stock solution: Heat high-purity silica (the content is greater than 99.9%) at a temperature of 1100 ¡ãC until its mass is constant, and cool to room temperature in a desiccator; weigh 2.1393 g and put it into a platinum crucible, add about 5 g of sodium carbonate, heat and melt for 15 minutes. Take it out and cool it slightly, place it in a 500 mL beaker, dissolve the melt with water, and wash out the platinum crucible; then, transfer the solution into a 1000 mL volumetric flask, wash the beaker with water and pour the washing liquid into the volumetric flask, add water to the scale of the volumetric flask, mix...
This standard specifies the type and size, technical condition and marking of the raised countersunk head screws with cross recess. This standard applies to the type H and type Z raised countersunk head screws with cross recess of the thread specification M1.6 ~ M10, the performance level of 4.8, A2-50, A2-70, CU2, CU3 and AL4, AND the product grade A.
This Part specifies the indoor test method for the longitudinal resistance of rails assembled with fasteners. This Part applies to fastening systems for high-speed railways. 2 Sign The following signs are applicable to this Document. D1: The maximum longitudinal displacement of the rail during the loading cycle, in millimeters (mm). D2: The residual longitudinal displacement of the rail after unloading, in millimeters (mm). D3: Elastic longitudinal displacement of the rail before sliding, in millimeters (mm). F: The longitudinal resistance of the rail, in kilonewtons (kN). 3 Principle Assemble the short rail with fasteners on the rail bearing surface of the anchored sleeper; and apply longitudinal tension to the rail; record the load and the longitudinal displacement of the rail relative to the sleeper; and unload when the rail slips. The longitudinal resistance of the rail is obtained from the load-displacement curve. 4 Test Equipment 4.1 Rails A section of short rail with a length of about 0.5 m, whose section is the same as that used for the assembly of the fastener to be tested or the assembly fatigue performance test. The rails shall be free from peeling, free from floating rust on the surface; and the bottom of the rails TB/T 3396.1-2015 www.ChineseStandard.net ? Buy True-PDF ? Auto-delivery. Page 5 of 9 shall not be polished due to repeated tests. 4.2 Loading device The device with the loading rate of 9kN/min ~ 11kN/min, and the static loading can reach 50kN, which applies the tension in the direction of the vertical sleeper through the bottom of the rail. 4.3 Displacement sensor An instrument for measuring the longitudinal displacement of the rail relative to the sleeper, with an indication error of 0.01 mm. 4.4 Load sensor An instrument for measuring the load applied to the rail, with an accuracy class of 0.5 4.5 Recording equipment For equipment capable of digitally recording and drawing load-displacement curves during the test, the sampling frequency shal...